Physical-Mechanical Properties of Superhard Nanocomposite Coatings on Base Zr-Ti-Si-N
|
|
| Creator |
Погребняк, Олександр Дмитрович
Погребняк, Александр Дмитриевич Pohrebniak, Oleksandr Dmytrovych Байдак, В. Baydak, V. Береснев, В.М. Beresnev, V.M. Турбин, П. Turbin, P. Махмудов, Н. Makhmudov, N. Ілляшенко, Максим Вікторович Ильяшенко, Максим Викторович Illiashenko, Maksym Viktorovych Колесников, Д. Kolesnikov, D. Ташметов, М. Tashmetov, M. |
|
| Subject |
nanocomposite
spinodal phase segregation compressive stress superhard |
|
| Description |
Hard and super hard coatings of Zr-Ti-Si-N of from 2.8 μm to 3.5 μm thickness were fabricated using a vacuum arc source with high frequency stimulation. The samples were annealed in vacuum and in air at 1200 °C. It was found that films with a high Zr and Ti content were thermally stable up to 1180 °C. At the same time, a thin oxide layer of 180 nm to 240 nm was found on the surfaces, which protected the sample from destruction. Below 1000 °C annealing temperature in vacuum, changing of phase composition is determined by appearing of siliconitride crystallites (ß-Si3N4) with hexagonal crystalline lattice and by formation of ZrO2 oxide crystallites. Size of grains of a substitution solid solution (Zr, Ti)N varied from (10 – 12) nm to 25 nm, but Ti concentration in the solid solution increased. In the process of annealing, hardness of the best series of samples increased from (39.6 ±1.4) GPa to 53.6 GPa, which seemed to indicate that a spinodal segregation along grain interfaces was finished. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/33942 |
|
| Date |
2014-02-12T08:56:49Z
2014-02-12T08:56:49Z 2013 |
|
| Type |
Article
|
|
| Identifier |
Physical-Mechanical Properties of Superhard Nanocomposite Coatings on Base Zr-Ti-Si-N [Текст] / O.D. Pohrebniak, V. Baydak, V.M. Beresnev [et al.] // Materials science (MEDŽIAGOTYRA). —2013. — Vol.19, №2. — P. 140-143
http://essuir.sumdu.edu.ua/handle/123456789/33942 |
|
| Language |
en
|
|