Effect of Electrodeposition Frequency on Magnetic Properties of (Co0.97Al0.03)0.7Fe0.3 Nanowires
Electronic Archive of Sumy State University
Переглянути архів Інформація| Поле | Співвідношення | |
| Title |
Effect of Electrodeposition Frequency on Magnetic Properties of (Co0.97Al0.03)0.7Fe0.3 Nanowires
|
|
| Creator |
Rafati, A.A.
Najafi, M. Zare, A. |
|
| Subject |
Nanowire
Magnetic properties Electrodeposition Frequency Anodic aluminum oxide membrane (AAO) |
|
| Description |
The magnetic properties of (Co0.97Al0.03)0.7Fe0.3 nanowires electrodeposited at different frequency of 50- 1000 Hz were studied. This nanowires were prepared by alternative current electrodeposition using porous anodic aluminum oxide as template. The results show that coercivity of samples slightly increased with increasing the frequency. Comparing the M–H hysteresis loops in different frequency shows that saturation magnetization (Ms) per unit area decreases with increasing the frequency. Magnetic properties were also investigated after annealing at 575 C. After annealing, a clear increase in coercivity was observed. |
|
| Publisher |
Sumy State University
|
|
| Date |
2014-05-29T06:24:51Z
2014-05-29T06:24:51Z 2012 |
|
| Type |
Article
|
|
| Identifier |
Rafati, A. A.
Effect of Electrodeposition Frequency on Magnetic Properties of (Co0.97Al0.03)0.7Fe0.3 Nanowires / A. A. Rafati, M. Najafi, A. Zare
// Nanomaterials: Applications & Properties (NAP-2012) : 2-nd International conference, Alushta, the Crimea, September 17-22, 2012 / Edited by: A. Pogrebnjak. - Sumy : Sumy State University, 2012. - V. 1, No4. - 04MFPN08
http://essuir.sumdu.edu.ua/handle/123456789/35345 |
|