Influence of chromium content in tempering steels on phase transition temperature A1 and A3
Електронний науковий архів Науково-технічної бібліотеки Національного університету "Львівська політехніка"
Переглянути архів Інформація| Поле | Співвідношення | |
| Title |
Influence of chromium content in tempering steels on phase transition temperature A1 and A3
|
|
| Creator |
Żmuda, Z.
|
|
| Subject |
phase transitions
heat treatable steels dilatometer tests alloying elements |
|
| Description |
For the three species of quenched and tempered steel (C50, 50Cr3, 51Cr6) dilatometric studies were conducted. They allowed the determination of transition temperatures Ac1 and Ac3 during heating and Ar3 and Ar1 during cooling. It was observed that increased the chromium content in steels tested resulted in an increase in transition temperature for heating and cooling. It was also observed narrow range of temperature from the beginning to the end of the transition with increasing chromium content.
|
|
| Date |
2014-02-14T11:04:01Z
2014-02-14T11:04:01Z 2013 |
|
| Type |
Article
|
|
| Identifier |
Żmuda Z. Influence of chromium content in tempering steels on phase transition temperature A1 and A3 / Z. Żmuda // Вісник Національного університету «Львівська політехніка». – 2013. – № 772 : Оптимізація виробничих процесів і технічний контроль у машинобудуванні та приладобудуванні. – С. 177-181. – Bibliography: 10 titles.
http://ena.lp.edu.ua:8080/handle/ntb/23542 |
|