ВЛИЯНИЕ ОКСИДОВ И ГИДРОКСИДОВ МЕТАЛЛОВ И ИХ НАНОРАЗМЕРНЫХ АНАЛОГОВ НА ОГНЕЗАЩИТНУЮ ЭФФЕКТИВНОСТЬ ИНТУМЕСЦЕНТНОЙ ПОЛИМЕРНОЙ КОМПОЗИЦИИ
Електронний архів E-archive DonNTU – (Electronic archive Donetsk National Technical University)
Переглянути архів Інформація| Поле | Співвідношення | |
| Title |
ВЛИЯНИЕ ОКСИДОВ И ГИДРОКСИДОВ МЕТАЛЛОВ И ИХ НАНОРАЗМЕРНЫХ АНАЛОГОВ НА ОГНЕЗАЩИТНУЮ ЭФФЕКТИВНОСТЬ ИНТУМЕСЦЕНТНОЙ ПОЛИМЕРНОЙ КОМПОЗИЦИИ
EFFECTS OF METAL OXIDES AND HYDROXIDES AND THEIR NANO SIZED ANALOGS ON FIRE PROTECTION EFFICIENCY OF INTUMESСENT POLYMERIC COMPOSITION |
|
| Creator |
Таран, Надежда Анатольевна
|
|
| Subject |
наноразмерные оксиды и гидроксиды металлов
антипирены интумесцентная композиция, огнезащитная эффективность коэффициент вспучивания nano-sized metal oxides ano-sized metal hydroxides intumescent composition fire protection efficiency intumescense coefficient antipyrenes |
|
| Description |
Исследованы интумесцентные композиции состава полифосфат аммония (ПАФ) / пентаэритрит (ПЭ) / меламин (МА) / сополимер винилацетата и этилена (ЭВА) с широким варьированием добавок оксидов, гидроксидов металлов и их наноразмерных аналогов. Выполнен сравнительный анализ влияния этих антипиренов на процессы формирования полимерного коксового слоя в интервале температур 200-600оС. Показано, что наиболее эффективными являются смеси, которые содержат в своем составе наночастицы оксидов титана и железа. Предложены наиболее вероятные механизмы химических превращений в интумесцентной системе с участием оксидов и гидроксидов металлов.
Intumescent systems involving a donor of phosphoric acid, polyol, and gas-forming agent are considered to be the most promising fire protection compositions. With decreasing temperature, an interaction of the ingredients results in formation of flame-proof foam-coke layer thus preventing the ignition and retarding or eliminating fire propagation at their early stages. Such systems exhibit low toxicity and fume-forming ability eliminate toxic action of halogen-containing components and increase the level of human and environmental protection from numerous adverse effects. Intumescent compositions involving ammonium polyphosphate/pentaerythritol/ melamine/vinyl acetate and ethylene copolymer at variable metal oxides and hydroxides and their nano-structured analogs were studied to develop new technologies for decreased combustibility of polymeric materials and fire protection coatings. Comparison examination of the antipyrene effects on the polymeric coke layer formation in a temperature range of 200-600 оС was carried out. It was shown that additives of metal oxides and hydroxides and their nano-sized analogs result in a considerable increase in fire protection efficiency of the intumescent composition ammonium polyphosphate/pentaerythritol/melamine/vinyl acetate and ethylene copolymer. The mixtures involving titanium oxide and iron oxide nanoparticles were found to be the most efficient. The most plausible mechanisms of the chemical transformations in the intumescent system involving metal oxides and hydroxides were proposed. Practical merit of the study consists in improving the development of thermally stable polymers and fire protection polymeric coatings. |
|
| Date |
2013-04-11T15:32:16Z
2013-04-11T15:32:16Z 2013 |
|
| Type |
Article
|
|
| Identifier |
2074-6652
УДК 667.637.4:699.81 http://ea.donntu.edu.ua/handle/123456789/18403 |
|
| Relation |
Наукові праці ДонНТУ;Серія: Хімія і хімічна технологія, 2013. - Вип.1(20). - С.102-108
|
|
| Publisher |
Донецк, ДонНТУ
|
|