Diagnostics of degradation of surfaces treated by thermal spraying
CUNTUR
Переглянути архів Інформація| Поле | Співвідношення | |
| Title |
Diagnostics of degradation of surfaces treated by thermal spraying
|
|
| Creator |
Greš, M.
Brezinová, J. Guzanová, A. |
|
| Contributor |
Technical University of Košice, Faculty of Mechanical Engineering, Košice, Slovakia
|
|
| Description |
The paper deals with possibilities of utilization HVOF coatings in thermal cyclic loading and wear conditions. There were evaluated three types of coatings based on WC-Co, WC-Co-Cr and Cr3C2-25NiCr. The quality of coatings was evaluated in terms of their adhesion during the cyclic thermal loading (pull-off test), microhardness and wear resistance (pin-on-disc test). Structure of coatings was studied using optical and electron microscopy. The coating Cr3C2-25NiCr showed the highest resistance to thermal cycles and wear resistance at 900°C and can be recommended for renovation components stressed by high and cyclic temperatures and wear. |
|
| Date |
2015-10-28T12:45:21Z
2015-10-28T12:45:21Z 2015-09-21 2015-09-21 |
|
| Type |
Article
|
|
| Identifier |
Diagnostics of degradation of surfaces treated by thermal spraying / M. Landová, M. Greš, J. Brezinová, A. Guzanová // IV міжнародна науково-технічна конференція „Пошкодження матеріалів під час експлуатації, методи його діагностування і прогнозування“ — Тернопіль : Вид-во ТНТУ імені Івана Пулюя, 2015. — С. 70-73. — (Діагностування пошкоджень).
http://elartu.tntu.edu.ua/handle/123456789/5960 Landová M., Greš M., Brezinová J., Guzanová A. Diagnostics of degradation of surfaces treated by thermal spraying. International Conference "In-Service Damage of Materials, its Diagnostics and Prediction", Ternopil, TNTU, 2015, P. 70-73 [in English]. |
|
| Language |
en
|
|
| Relation |
Матеріали IV міжнародної науково-технічної конференції „Пошкодження матеріалів під час експлуатації, методи його діагностування і прогнозування“
1. M. Li, P. D. Christofides, Chem. Eng. Sci. 61 (2006) 6540-6552. 2. T. Sahraoui, S. Guessasma, , N.E. Fenineche, G. Montavon, C. Coddet, Mater. Lett. 58 (2004) 654-660. 3. R. J. K. Wood, Int. J. Refract. Met. Hard Mater. 28 (2010) 82-94. 4. L. Thakur, N. Arora, R. Jayaganthan, R. Sood, Appl. Surf. Sci. 258 (2011) 1225-1234. 5. W. Žórawski, Surf. Coat. Technol. 220 (2013) 276-281. 6. T. Sahraoui, S. Guessasma, M. A. Jeridane, M. Hadji, Mater. Des. 31 (2010) 1431 – 1437. 7. V.A.D. Souza, A. Neville, Wear 259 (2005) 171-180. 1. M. Li, P. D. Christofides, Chem. Eng. Sci. 61 (2006) 6540-6552. 2. T. Sahraoui, S. Guessasma, , N.E. Fenineche, G. Montavon, C. Coddet, Mater. Lett. 58 (2004) 654-660. 3. R. J. K. Wood, Int. J. Refract. Met. Hard Mater. 28 (2010) 82-94. 4. L. Thakur, N. Arora, R. Jayaganthan, R. Sood, Appl. Surf. Sci. 258 (2011) 1225-1234. 5. W. Žórawski, Surf. Coat. Technol. 220 (2013) 276-281. 6. T. Sahraoui, S. Guessasma, M. A. Jeridane, M. Hadji, Mater. Des. 31 (2010) 1431 – 1437. 7. V.A.D. Souza, A. Neville, Wear 259 (2005) 171-180. |
|
| Rights |
© Тернопільський національний технічний університет імені Івана Пулюя, 2015
|
|
| Format |
70-73
|
|
| Coverage |
Тернопіль
Ternopil |
|
| Publisher |
Вид-во ТНТУ імені Івана Пулюя
|
|